Data sheet
Bulk density: 2.70 grs / cm 3
Absorption Coefficient: 0.15%
Porosity: 0.10%
Res.mec. At compression: 1250 kg / cm 2 .
Res.mec. At bending: 195 kg / cm 2
Wear resistance: 0.35 mm.
Impact resistance: 42 cm
Knoop microhardness: 180 Kg / mm 2
Kavala medium white
Data sheet
Petrographic denomination: Calcitic Marble
Apparent Density (KG / m 3 ): 2690
Open porosity (%): 0.9
Absorption of water at atmospheric pressure (%): 0.13
Water vapor permeability: 10000
Resistance to Fexion (Mpa): 11.6
Slip Resistance: 44
Reaction to fire: Class A
White carrara
Data sheet
Densité apparente (kg / m 3 ): 2680
Résistance à la compression (Mpa): 2810
Résistance à la flexion (Mpa): 3.8
Résistance à l'abrasion (mm): 0,35
Résistance aux chocs (cm): 9,6
Coefficient d'absorption (% en poids) 10 000
White Spider
Data sheet
Water Absorption: 0,19 by weight %
Compressive Strength: 137,34 - 140,0 Mpa
Density: 2825 Kg/m3
Flexural Strength: 6,0 - 8,87 Mpa
APPARENT SPECIFIC DENSITY, kg/m3 (DIN 52102) 2825
OPEN POROSITY COEFFICIENT, % vol (DIN 52102) 0,54
WATER ABSORPTION COEFFICIENT, % WT (din 52103) 0,19
DYNAMIC MODULUS OF ELASTICITY, GPa (DIN 1048 Teil 5) 35
COMPRESSIVE STRENGTH, MPa (DIN 52105) 139
FLESURAL STRENGTH AFTER FREEZE/THAW CYCLES, MPa (DIN 52104 & 52105) 103
ABRASION RESISTANCE, mm (DIN 52108) 2,20
IMPACT STRENGTH, cm (UNI-U 32.07.248.0) 59
MINERALOGICAL COMPOSITION, % wt
CALCITE 8,0
DOLOMITE 92,00
CHEMICAL ANALYSIS, % wt
CALCITE 8,00
DOLOMITE 92,00
CHEMICAL ANALYSIS, % wt
CaO 32 MgO 19,60 SiO2 0,20
Fe203 <0,05 AI203 <0,05 K2O <0,01
Na2O 0,01 MnO <0,01 LOI 46,90