Back to Marble and Limestones
capri/marbella
Data sheet
Composition: Limestone Oolitic
Fosiles Apparent specific weight: 2.44 Grs / Cm2
Absorption Rate: 8.90%
Apparent Porosity: 11.43%
Impact resistance: 34.60 Cm
Wear resistance: 8.60 M.M.
Compressive strength: 836.7 Kgs / Cm2
flexural strength to 148.90 Kgs / Cm2
Cream – Beige Large size of grain
Low tolaidad changes
High uniformity marbled Grainy honeycombs 1
Related Products
Alba
Data sheet
Apparent specific weight: 2.25 g / cm3
Apparent Porosity: 11.71%
Absorption coefficient: 5.21%
Mechanical compressive strength: 53.8 MPa
mechanical bending strength: 5.0 MPa
Resistance to frost: 0.07%
Resistance to thermal changes: 0.04%
Shock resistance: 22.0 cm
Knoop microhardness: 0
Ivory cream
Data sheet
Volumetric mass: 2.72 g / cm³
Absorption coefficient: 0.15%
Open Porosity: 0.10%
mechanical compressive strength: 122.84%
mechanical compressive strength after frost resistance:%
Mechanical resistance to flexion: 19.41 Mpa
Anchoring resistance: N
Wear resistance: 0.35 mm.
Resitencia slip (polished surface): USRV
Impact resistance: 42 joules
Knoop microhardness: 1774.5 Mpa
Black marquina
Data sheet
SPECIFIC GRAVITY 2.69 g / cm3
ABSORPTION COEFFICIENT 0.17%
COMPRESSION RESISTANCE 629 kg / cm2
Flexural strength 136 kg / cm2
RESISTANCE TO WEAR 2.90 mm.
IMPACT RESISTANCE 30 cm.
MODULE Frosting n / d THERMAL n / d
ORIGIN MARQUINA (VIZCAYA)
Alicante red
Data sheet
Volumetric mass: 2.71 g / cm³
Absorption coefficient: 0.10%
Open Porosity: 0.3%
mechanical compressive strength: 94.61%
mechanical compressive strength after frost resistance:%
mechanical bending strength: 8.73
Mpa Anchoring resistance: N
Wear resistance: 2,42 mm.
Resitencia slip (polished surface): USRV
Impact resistance: 30 joules
Knoop microhardness: 1500 Mpa