White carrara
Data sheet
Densité apparente (kg / m 3 ): 2680
Résistance à la compression (Mpa): 2810
Résistance à la flexion (Mpa): 3.8
Résistance à l'abrasion (mm): 0,35
Résistance aux chocs (cm): 9,6
Coefficient d'absorption (% en poids) 10 000
White Sivec
Data sheet
Resistance to crushing when dry (N/mm2): 191.5/143.7
Resistance to crushing when wet (N/mm2): 182.3/133.1
Resistance to cooling -defrosting /N/mm2): 174.0/129.0
Resistance to bending (N/mm2): 9.33/8.14
Resistance to colision: 8/10
Abrasion rate (cm250 cm): 40/15
Water absorption rate (%): 0.14/0.12
Special wight (g/cm2): 2.79/2.88
Density (g/cm2): 2.88/2.82
Extent of elasticity (MPa): 84.5/79.1
Porosity(%): 0.50
White Spider
Data sheet
Water Absorption: 0,19 by weight %
Compressive Strength: 137,34 - 140,0 Mpa
Density: 2825 Kg/m3
Flexural Strength: 6,0 - 8,87 Mpa
APPARENT SPECIFIC DENSITY, kg/m3 (DIN 52102) 2825
OPEN POROSITY COEFFICIENT, % vol (DIN 52102) 0,54
WATER ABSORPTION COEFFICIENT, % WT (din 52103) 0,19
DYNAMIC MODULUS OF ELASTICITY, GPa (DIN 1048 Teil 5) 35
COMPRESSIVE STRENGTH, MPa (DIN 52105) 139
FLESURAL STRENGTH AFTER FREEZE/THAW CYCLES, MPa (DIN 52104 & 52105) 103
ABRASION RESISTANCE, mm (DIN 52108) 2,20
IMPACT STRENGTH, cm (UNI-U 32.07.248.0) 59
MINERALOGICAL COMPOSITION, % wt
CALCITE 8,0
DOLOMITE 92,00
CHEMICAL ANALYSIS, % wt
CALCITE 8,00
DOLOMITE 92,00
CHEMICAL ANALYSIS, % wt
CaO 32 MgO 19,60 SiO2 0,20
Fe203 <0,05 AI203 <0,05 K2O <0,01
Na2O 0,01 MnO <0,01 LOI 46,90