Alba
Alba
Data sheet
Apparent specific weight: 2.25 g / cm3 Apparent Porosity: 11.71% Absorption coefficient: 5.21% Mechanical compressive strength: 53.8 MPa mechanical bending strength: 5.0 MPa Resistance to frost: 0.07% Resistance to thermal changes: 0.04% Shock resistance: 22.0 cm Knoop microhardness: 0
Read More
Golden lift
Golden lift
Data sheet
Bulk density: 2.70 grs / cm 3 Absorption Coefficient: 0.15% Porosity: 0.10% Res.mec. At compression: 1250 kg / cm 2 . Res.mec. At bending: 195 kg / cm 2 Wear resistance: 0.35 mm. Impact resistance: 42 cm Knoop microhardness: 180 Kg / mm 2
Read More
Kavala medium white
Kavala medium white
Data sheet
Petrographic denomination: Calcitic Marble Apparent Density (KG / m 3 ): 2690 Open porosity (%): 0.9 Absorption of water at atmospheric pressure (%): 0.13 Water vapor permeability: 10000 Resistance to Fexion (Mpa): 11.6 Slip Resistance: 44 Reaction to fire: Class A
Read More
White carrara
White carrara
Data sheet
Densité apparente (kg / m 3 ): 2680 Résistance à la compression (Mpa): 2810 Résistance à la flexion (Mpa): 3.8 Résistance à l'abrasion (mm): 0,35 Résistance aux chocs (cm): 9,6 Coefficient d'absorption (% en poids) 10 000
Read More
White Sivec
White Sivec
Data sheet
Resistance to crushing when dry (N/mm2): 191.5/143.7 Resistance to crushing when wet (N/mm2): 182.3/133.1 Resistance to cooling -defrosting /N/mm2): 174.0/129.0 Resistance to bending (N/mm2): 9.33/8.14 Resistance to colision: 8/10 Abrasion rate (cm250 cm): 40/15 Water absorption rate (%): 0.14/0.12 Special wight (g/cm2): 2.79/2.88 Density (g/cm2): 2.88/2.82 Extent of elasticity (MPa): 84.5/79.1 Porosity(%): 0.50
Read More
White Spider
White Spider
Data sheet
Water Absorption: 0,19 by weight % Compressive Strength: 137,34 - 140,0 Mpa Density: 2825 Kg/m3 Flexural Strength: 6,0 - 8,87 Mpa APPARENT SPECIFIC DENSITY, kg/m3 (DIN 52102) 2825 OPEN POROSITY COEFFICIENT, % vol (DIN 52102) 0,54 WATER ABSORPTION COEFFICIENT, % WT (din 52103) 0,19 DYNAMIC MODULUS OF ELASTICITY, GPa (DIN 1048 Teil 5) 35 COMPRESSIVE STRENGTH, MPa (DIN 52105) 139 FLESURAL STRENGTH AFTER FREEZE/THAW CYCLES, MPa (DIN 52104 & 52105) 103 ABRASION RESISTANCE, mm (DIN 52108) 2,20 IMPACT STRENGTH, cm (UNI-U 32.07.248.0) 59 MINERALOGICAL COMPOSITION, % wt CALCITE 8,0 DOLOMITE 92,00 CHEMICAL ANALYSIS, % wt CALCITE 8,00 DOLOMITE 92,00 CHEMICAL ANALYSIS, % wt CaO 32 MgO 19,60 SiO2 0,20 Fe203 <0,05 AI203 <0,05 K2O <0,01 Na2O 0,01 MnO <0,01 LOI 46,90
Read More