Limestones Novelda, Alicante province

Alba
Alba
Data sheet
Apparent specific weight: 2.25 g / cm3 Apparent Porosity: 11.71% Absorption coefficient: 5.21% Mechanical compressive strength: 53.8 MPa mechanical bending strength: 5.0 MPa Resistance to frost: 0.07% Resistance to thermal changes: 0.04% Shock resistance: 22.0 cm Knoop microhardness: 0
Read More
Alicante red
Alicante red
Data sheet Volumetric mass: 2.71 g / cm³ Absorption coefficient: 0.10% Open Porosity: 0.3% mechanical compressive strength: 94.61% mechanical compressive strength after frost resistance:% mechanical bending strength: 8.73 Mpa Anchoring resistance: N Wear resistance: 2,42 mm. Resitencia slip (polished surface): USRV Impact resistance: 30 joules Knoop microhardness: 1500 Mpa
Read More
Black marquina
Black marquina
Data sheet SPECIFIC GRAVITY 2.69 g / cm3 ABSORPTION COEFFICIENT 0.17% COMPRESSION RESISTANCE 629 kg / cm2 Flexural strength 136 kg / cm2 RESISTANCE TO WEAR 2.90 mm. IMPACT RESISTANCE 30 cm. MODULE Frosting n / d THERMAL n / d ORIGIN MARQUINA (VIZCAYA)
Read More
Brown Emperor
Brown Emperor
Data sheet
Bulk density: 2.65 grs / cm3 Absorption coefficient: 0.40% Porosity: 1.20% Mech. Res. At compression: 1,597 Kg / cm2 Mech. Res. At bending: 210 Kg./cm2 Wear resistance: 0.55 mm. Impact resistance: 35 cm Knoop Microhardness: 157 Kg./mm2
Read More
capri/marbella
capri/marbella
Data sheet Composition: Limestone Oolitic Fosiles Apparent specific weight: 2.44 Grs / Cm2 Absorption Rate: 8.90% Apparent Porosity: 11.43% Impact resistance: 34.60 Cm Wear resistance: 8.60 M.M. Compressive strength: 836.7 Kgs / Cm2 flexural strength to 148.90 Kgs / Cm2 Cream - Beige Large size of grain Low tolaidad changes High uniformity marbled Grainy honeycombs 1
Read More
Guatemala green
Guatemala green
Data sheet Volumetric mass 2,73 g / cm³ Absorption coefficient 0.33% Mechanical resistance to compression 2,031 kg / cm² Mechanical resistance to bending 265 kg / cm²
Read More
Ivory cream
Ivory cream
Data sheet Volumetric mass: 2.72 g / cm³ Absorption coefficient: 0.15% Open Porosity: 0.10% mechanical compressive strength: 122.84% mechanical compressive strength after frost resistance:% Mechanical resistance to flexion: 19.41 Mpa Anchoring resistance: N Wear resistance: 0.35 mm. Resitencia slip (polished surface): USRV Impact resistance: 42 joules Knoop microhardness: 1774.5 Mpa
Read More
Light emperor
Light emperor
Data sheet
Volumetric mass: 2.79 g / cm³ Absorption coefficient: 0.10% Open Porosity: 1.20% mechanical compressive strength: 154.9% mechanical compressive strength after frost resistance:% Mechanical resistance to flexion: 21.18 Mpa Anchoring resistance: N Wear resistance: 0.50 mm. Resitencia slip (polished surface): USRV Impact resistance: 35 joules Knoop microhardness: 14.51 Mpa
Read More